Polyethylene flame-retardant masterbatch

This product is based on polyethylene and supplemented with flame retardants, antioxidants and other additives, and is made through mixing, plasticizing and granulation. It is mainly applied in the production and manufacturing of silane cross-linked polyethylene overhead insulated cables to improve and enhance the flame retardant performance of the cables. The specific addition amount is determined based on the flame retardant requirements of the cables.

Contact Download

Product details

Product model and name

Model	Product name	Main application fields
ZPE-1	Polyethylene flame-retardant masterbatch	Applicable to aluminum alloy conductors
ZPE-2	Polyethylene flame-retardant masterbatch	Applicable to copper and aluminum alloy conductors
ZPE-4	Polyethylene flame-retardant masterbatch	Applicable to aluminum alloy conductors

Application process reference

It is recommended that the temperature of the extruder body be 150℃-180℃. Neck temperature: 180℃ Head temperature: 180℃-190℃. The above is the recommended temperature. Adjust it according to the actual plasticizing situation.

Packaging and storage

The product is packed in moisture-proof aluminum foil/polyethylene composite film bags, with each bag weighing 25kg. And single-pallet palletizing transportation is adopted. The net weight specifications of single-pallet palletizing are 1000kg, 1250kg and 1500kg.

It should be stored in a clean, dry and well-ventilated environment, with an appropriate storage temperature ranging from 0℃ to 35℃.

The validity period is 6 months when the packaging is sealed. After opening, it is recommended to use it up within 24 hours to avoid moisture affecting the quality of use.