Silane crosslinked polyethylene insulating material for one-step cable YJG

This product takes linear low-density polyethylene as the main raw material, and adds catalytic masterbatch, additives, etc., through a single process of specific process, it is mainly used for the production of 10kV and below overhead insulated cables.

Contact Download

Product details

Performance indicators (typical values)： enforce standards：JB/T 10260-2014

Serial number	Pilot project		unit	YJG
1	Tensile strength ≥		Mpa	13.0
2	Fracture elongation green ≥		%	300
3	Impact embrittlement (-76℃)≤		N/A	15/ 30
4	135℃, 168h air thermal aging	Variation rate of tensile strength≤	%	±20
4	135℃, 168h air thermal aging	Rate of change of elongation at break≤	%	±20
5	Thermal elongation 200℃,0.2MPa, 15min	Thermal elongation≤	%	175
5	Thermal elongation 200℃,0.2MPa, 15min	Permanent deformation rate after cooling≤	%	15
6	50Hz、20℃	Relative dielectric constant≤		/
6	50Hz、20℃	Dielectric loss factor≤		0.001
7	Volume resistivity (1 kV, 20℃)≥		Ω·cm	5.0×1013
8	Dielectric strength≥		MV/ m	25
9	Gel content≥		%	/

Application process reference

Recommended extruder body temperature: 160℃~200℃; Neck temperature: 200℃; Head temperature: 210℃~215℃.

Crosslinking condition

Crosslinking condition	temperature	Insulation thickness (1mm)
Warm water crosslinking	≥90℃	≥4小时
Steam crosslinking	≥90℃	≥6小时

Packaging and storage

1. 1. The product is packed with impervious aluminum foil/polyethylene composite film bag, which usually has a net weight of 25kg and is packed into a single unit, and is transported by single pallet palletizing. The net weight specifications of single pallet palletizing are 1000kg, 1250kg and 1500kg.

2. Should be stored in a clean, dry and ventilated environment, suitable for storage temperature 0℃ ~ 35℃.

3. The validity period is 6 months under the sealed condition, and it is recommended to use within 24 hours after opening. If the recommended time limit is exceeded, the quality is easily affected by pre-crosslinking.