Peroxide cross-linked easily peelable semiconductive shielding material for 35kV and below cross-lin

This product is mainly applicable to the peroxide cross-linked easy-peel type semiconductive insulation shielding for 35kV cross-linked polyethylene insulated cables, with low peel strength.

Contact Download

Product details

Product model and name:

PYJBJ-Y-35 Peroxide cross-linked easily peelable semiconductive shielding material for 35kV and below cross-linked polyethylene insulated cables

Performance indicators (typical values)： enforce standards JB/T 10738-2007

Serial number	Test project		Unit	Indicator	PYJBJ-Y-35
1	Density		g/cm3	≤1.2	1.13
2	Tensile strength		MPa	≥10.0	13
3	Elongation at break		%	≥200	255
4	Air thermal aging	Thermal aging conditions	/	135℃×168h
		Rate of change of tensile strength	%	±30	＋6
		Rate of change in elongation at break	%	±30	－13
5	（-40℃）Impact embrittlement performance		Number of failures	≤15/30	0/30
6	Thermal extension	Thermal extension conditions		200℃×0.2MPa×15min
		Elongation under load	%	≤100	60
		Permanent deformation after cooling	%	≤15	0
7	Volume resistivity at 20℃		Ω.cm	≤100	55
8	Volume resistivity at 90℃		Ω.cm	≤2500	950
9	Air thermal aging	Thermal aging conditions	/	100℃×168h
9	Air thermal aging	Volume resistivity at 90℃	Ω.cm	≤500	400
10	Peel strength（23℃）		N/cm	≤10-45	20
11	Air thermal aging	Thermal aging conditions	/	100℃×168h
11	Air thermal aging	Peel strength（23℃）	N/cm	10-45	18

Application process reference

It is recommended that the temperature of the extruder body be between 70℃ and 100℃. Neck temperature: 100℃ to 105℃ Head temperature: 100℃ to 105℃. It is recommended to use a 20× 60-mesh double-layer filter screen.

Packaging and storage

1) The product is packed in a waterproof and dustproof PE inner bag, supplemented by a hard corrugated carton for shaping and protection, and an additional waterproof film cover. The standard net weight of each box is 500kg or 600kg.

2) It should be stored in a clean, dry and well-ventilated environment, with an appropriate storage temperature ranging from 0℃ to 35℃.

3) The stacking height should not exceed two layers, and the upper and lower layers should be neatly stacked. It is not advisable to stack them in a staggered manner.

The validity period is 6 months under suitable storage conditions.