Modified polypropylene insulating material for power cables of 10kV and below PJ-10

This product is mainly made of polypropylene resin through mixing, plasticizing and granulation. It is a non-cross-linked cable insulation material, mainly used for insulation of power cables of 10kV and below. Compared with the conventional cross-linked polyethylene cable insulation materials, it has its unique circular economy advantages.

Contact Download

Product details

Performance indicators (typical values)： enforce standards：T/SHPTA 014. 1 -2021

Serial number	Experimental project		Standard	Typical value
1	Appearance		It is in the form of 3x4mm round or shoulder-round particles, with uniform size and color, no coke particles, and no obvious powder substances	"Conforms to"
2	Volume resistivity(20℃)		≥1 × 1014 ( Ω·m)	2.4x1014
3	Volume resistivity(90℃)		≥3 × 101 1 ( Ω·m)	4.8x1011
4	Volume resistivity(105℃)		≥1 × 101 0 ( Ω·m)	2.1 × 1010
5	Dielectric loss Angle tangent(20 ° C51Hz)		≤1x10- 3	9.8× 10- 4
6	Dielectric strength(20℃)		≥35( MV/ m)	37
7	Tensile strength		≥13. 5 ( Mpa)	21.8
8	Elongation at break		≥350(%)	537
9	Density			0.875
10	Thermal deformation		≤40%	1.5
11	Low-temperature embrittlement temperature(-76℃)		≤15/ 30	0/ 30
12	Thermal aging 150℃168h	Rate of change of tensile strength	≤±25(%)	-16.8
12	Thermal aging 150℃168h	Rate of change in elongation at break	≤±25(%)	-13.2

Application process reference

It is recommended that the temperature of the extruder body be between 160℃ and 200℃. Neck temperature: 200℃ Head temperature: 210℃ to 215℃.

Packaging and storage

The product is packed in a waterproof and dustproof PE inner bag, with a hard corrugated carton for shaping and protection, and an additional waterproof film cover. The standard net weight of each box is 500kg or 600kg.

It should be stored in a clean, dry and well-ventilated environment, with an appropriate storage temperature ranging from 0℃ to 35℃.

3. The stacking height should not exceed two layers, and the upper and lower layers should be neatly stacked. It is not advisable to stack them in a staggered manner.

The validity period is 6 months under suitable storage conditions.