Silane cross-linked polyethylene insulation material for cables (Carbon Black 2.0)YJG

This product is mainly made of linear low-density polyethylene, with the addition of coupling agents and other additives, and is produced through mixing, plasticizing and granulation. The two-step production process is adopted. Among them, Component A is the grafting material and Component B is the catalytic masterbatch. Adding a certain proportion of carbon black improves the weather resistance of the product. It is mainly used for the production of overhead insulated cables of 10kV and below.

Contact Download

Product details

Performance indicators (typical values)： enforce standards：JB/T 10260-2014

Serial number	Test project		Unit	YJG
1	Tensile strength ≥		Mpa	13.0
2	Fracture elongation green ≥		%	300
3	Impact embrittlement performance(-76℃)≤		N/A	15/ 30
4	135℃ , 168h Air thermal aging	Rate of change of tensile strength≤	%	±20
4	135℃ , 168h Air thermal aging	Rate of change in elongation at break≤	%	±20
5	Thermal extension 200℃,0.2MPa, 15min	Thermal extension≤	%	175
5	Thermal extension 200℃,0.2MPa, 15min	Permanent deformation rate after cooling≤	%	15
6	50Hz、20℃	Relative dielectric constant≤		/
6	50Hz、20℃	Dielectric loss factor≤		0.001
7	Volume resistivity(1 kV、20℃)≥		Ω·cm	5.0×1013
8	Dielectric strength≥		MV/ m	25
9	Gel content≥		%	/

Application process reference

It is recommended that the temperature of the extruder body be between 160℃ and 200℃. Neck temperature: 200℃ Head temperature: 210℃ to 215℃.

Crosslinking conditions

Crosslinking conditions	Temperature	Insulation thickness (1mm)
Warm water cross-linking	≥90℃	≥4h
Steam crosslinking	≥90℃	≥6h

Packaging and storage

The product is packed in moisture-proof aluminum foil/polyethylene composite film bags. Usually, the AB combination net weight is 25kg per unit and is transported by single-pallet palletizing. The net weight specifications of single-pallet palletizing are 1000kg, 1250kg and 1500kg.

It should be stored in a clean, dry and well-ventilated environment, with an appropriate storage temperature ranging from 0℃ to 35℃.

The validity period is 6 months when the packaging is sealed. After opening, it is recommended that Component A be used within 24 hours, and the mixture of A and B should be used within 8 hours. Exceeding the recommended time limit may affect the quality of use due to pre-crosslinking.