Silane crosslinked polyethylene insulating material for cables up to and including 3kV by one-step p

This product takes linear low-density polyethylene as the main raw material, and adds catalytic masterbatch, additives, etc., through a single process of specific processing, mainly used for the production of 3kV and below low-voltage cables and control cables.

Contact Download

Product details

Performance indicators (typical values)： enforce standards：JB/T 10437-2004

Serial number	Pilot project		unit	YJG-3
1	Tensile strength ≥		Mpa	13. 5
2	Fracture elongation green ≥		%	350
3	Impact embrittlement performance (-76℃)≤		N/A	15/ 30
4	135℃, 168h air thermal aging	Tensile strength change rate ≤	%	±20
4	135℃, 168h air thermal aging	Elongation at break change rate ≤	%	±20
5	Thermal elongation 200℃,0.2MPa, 15min	Thermal elongation ≤	%	100
5	Thermal elongation 200℃,0.2MPa, 15min	Permanent deformation rate after cooling ≤	%	5
6	Volume resistivity (1 kV, 20℃)≥		Ω·cm	1.0× 1014
7	Dielectric strength ≥		MV/ m	25
8	Gel content ≥		%	60

Application process reference

Recommended extruder body temperature: 160℃~200℃; Neck temperature: 200℃; Head temperature: 210℃~215℃.

Crosslinking condition

Crosslinking condition	temperature	Insulation thickness (1mm)
Warm water crosslinking	≥90℃	≥4h
Steam crosslinking	≥90℃	≥6h

Packaging and storage

1. 1. The product is packed with impervious aluminum foil/polyethylene composite film bag, which usually has a net weight of 25kg and is packed into a single unit, and is transported by single pallet palletizing. The net weight specifications of single pallet palletizing are 1000kg, 1250kg and 1500kg.

2. Should be stored in a clean, dry and ventilated environment, suitable for storage temperature 0℃ ~ 35℃.

3. The validity period of the package is 6 months in the closed state, and it is recommended to use within 24 hours after opening. If the recommended time limit is exceeded, the quality of use will be affected by pre-crosslinking.